Niklisulamid Elektroodide ENi-1 käsitsi valmistamine
KEEMILINE KOMPONET:
| SULAM (massi%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| GB/T REEGLID | 0.10 | 0,75 | 1.20 | ≥92 | 0,70 | 1,0-4,0 | 0,20 | 0,02 | 0,015 |
| AWS-i reeglid | 0.10 | 0,75 | 1.25 | ≥92 | 0,75 | 1,0-4,0 | 0,25 | 0,03 | 0,02 |
| NÄIDISVÄÄRTUS | 0,046 | 0,06 | 0,82 | 95,5 | 0.12 | 2.7 | 0,01 | 0,007 | 0,001 |
MEHAANILINE OMADUS:
| KINNISVARA | SAAGITUGUS (MPa) | PIKENDUSE TUGUS (MPa) | IMAPACT VALUE J/℃ | PIKEMINE (%) | ||||
| GB/T REEGLID | 200 | 410 | - | 18 | ||||
| AWS-i reeglid | - | 410 | - | 20 | ||||
| NÄIDISVÄÄRTUS | 310 | 435 | - | 29 | ||||
SOOVITATAVAD KEEVITUSPARAMEERID:
| LÄBIMEETRI TEHNILISED ANDMED (mm) | 2,6*300 | 3,2*350 | 4,0*350 | |||||||
| ELEKTER (Amper) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Titaan-kaltsium käsielektrood, nimikoostis (massiprotsent) on 95Ni-2,5Ti.
Stabiilne kaar, ilus vormimine, vähe pritsmeid, lihtne räbu eemaldamine, hea poorsuskindlus.
Sulatatud metallil on head mehaanilised omadused, kuumakindlus, korrosioonikindlus, sulamis- ja pragunemiskindlus.
Nafta rafineerimisseadmetes kasutatakse laialdaselt Cr-Mo teraseseeria keevitusmaterjale ja elektroodide pinnakatte keevitusmaterjale
-
158 000 tonni Suessi tanker
Supercore SG
KEEMILINE KOMPONET:
| SULAM (massi%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| GB/T REEGLID | 0.10 | 0,75 | 1.20 | ≥92 | 0,70 | 1,0-4,0 | 0,20 | 0,02 | 0,015 |
| AWS-i reeglid | 0.10 | 0,75 | 1.25 | ≥92 | 0,75 | 1,0-4,0 | 0,25 | 0,03 | 0,02 |
| NÄIDISVÄÄRTUS | 0,046 | 0,06 | 0,82 | 95,5 | 0.12 | 2.7 | 0,01 | 0,007 | 0,001 |
MEHAANILINE OMADUS:
| KINNISVARA | SAAGITUGUS (MPa) | PIKENDUSE TUGUS (MPa) | IMAPACT VALUE J/℃ | PIKEMINE (%) | ||||
| GB/T REEGLID | 200 | 410 | - | 18 | ||||
| AWS-i reeglid | - | 410 | - | 20 | ||||
| NÄIDISVÄÄRTUS | 310 | 435 | - | 29 | ||||
SOOVITATAVAD KEEVITUSPARAMEERID:
| LÄBIMEETRI TEHNILISED ANDMED (mm) | 2,6*300 | 3,2*350 | 4,0*350 | |||||||
| ELEKTER (Amper) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Kirjutage oma sõnum siia ja saatke see meile